- After UV light exposure (with certain wave length), the adhesion is greatly reduced (irreversible reaction), the object can be easily removed and picked up.
- Used for any production process.
- Different release liner design for distinguish A & B sides.
- Low energy release, speed up the production process.
- Anti-static version is available.
| Model | Material | Physical Property | Applications | ||
| UDD105P | PET film Double sided UV Release adhesive |
Total thickness | 120 ± 7 | µm | Production process improvement. |
| A side before curing adhesion | 0.3 ± 0.2 | kg/in | |||
| A side after curing adhesion | 0.02↓ | kg/in | |||
| B side before curing adhesion | 0.3 ± 0.2 | kg/in | |||
| B side after curing adhesion | 0.02↓ | kg/in | |||
| UTD502-2 | PET film Double sided A side UV release B side thermal release |
Total thickness | 115 ± 6 | µm | Production process Improvement. Thermal release side: 90°C-3min |
| UV side before curing adhesion | 0.7 ± 0.3 | kg/in | |||
| UV side after curing adhesion |
0.03↓ | kg/in | |||
| Before thermal release adhesion |
0.5 ± 0.3 | kg/in | |||
| After thermal release adhesion |
0.01↓ | kg/in | |||
| UDE145 | PET film Double sided A side UV release B side PSA |
Total thickness | 145 ± 8 | µm | Production process improvement. |
| A side before curing adhesion | 1.8↑ | kg/in | |||
| A side after curing adhesion | 0.05↓ | kg/in | |||
| B side PSA adhesion | 0.15↑ | kg/in | |||